'custom quotation'

Half Round Tube Shield Ladhani Metal Corporation manufactures high-quality Half Round Tube Shields designed to protect boiler and heat exchanger tubes from erosion, scaling, and thermal fatigue. These shields are especially suited for systems where tubes are exposed to turbulent gas flow, particulate-laden environments, and fluctuating thermal cycles. The semi-cylindrical shape of the shield allows easy installation and reliable surface protection, extending the operational life of the tubes. 1Cr13 Half Round Tube Shield for LTSH Tube The 1Cr13 Half Round Tube Shield is fabricated from martensitic stainless steel containing approximately 13% chromium. Known for its good corrosion resistance, moderate heat resistance, and excellent wear strength, 1Cr13 is suitable for medium-temperature applications, especially in mildly corrosive or oxidizing environments. This makes it an ideal material for shielding LTSH (Low Temperature Superheater) tubes from flue gas erosion and ash abrasion. The Low Temperature Superheater (LTSH) is a section in a boiler where saturated steam from the steam drum is superheated to a moderately higher temperature before entering the high-temperature superheater stages. Positioned in areas with relatively lower flue gas temperatures, the LTSH helps improve thermal efficiency and reduces moisture content in steam. Due to constant exposure to abrasive flue gases and ash, LTSH tubes are prone to wear and require protective shielding, such as half round tube shields, to extend service life. Ladhani Metal Corporation is a reliable manufacturer, supplier, and exporter of 1Cr13 Half Round Tube Shields, delivering durable and cost-effective solutions for various thermal power and heat exchanger applications. Chemical Composition of 1Cr13 – Martensitic Stainless Steel • Carbon (C): 0.15 – 0.20% • Manganese (Mn): ≤ 1.00% • Phosphorus (P): ≤ 0.040% • Sulfur (S): ≤ 0.030% • Silicon (Si): ≤ 1.00% • Chromium (Cr): 12.0 – 14.0% • Iron (Fe): Balance Applications: Suitable for moderately corrosive and abrasive environments, especially in boiler systems, where mechanical strength and oxidation resistance are required at elevated but controlled temperatures. Uses • Protection of LTSH tubes in thermal power plant boilers • Surface shielding in steam generators and utility boilers • Coverage of superheater coils in flue gas-exposed zones • Suitable for coal-fired and biomass-fired boiler applications • Used in refinery and petrochemical boilers with moderate gas exposure Features • Good corrosion and oxidation resistance – Provides reliable performance in mildly corrosive environments • Wear and erosion resistance – Withstands mechanical wear from ash and soot-laden gas streams • Precise custom fitting – Fabricated to match specific tube diameters and bend radii • Enhanced tube protection – Minimizes wear on LTSH tubes, increasing overall system lifespan • Easy installation – Supports clamp-on, weld-on, and banding installation options • Wide availability – Offered in various lengths, thicknesses, and profiles Applications • power generation – Used in LTSH zones to protect from flue gas erosion and slagging • WHRBs – Shields exposed surfaces of tube bends in waste heat recovery systems • chemical and fertilizer plants – Applied in steam systems requiring moderate temperature durability • cement industry – Suitable for boilers dealing with particulate exhaust gas environments • industrial utility boilers – Enhances tube life in fluctuating thermal load zones Conclusion The 1Cr13 Half Round Tube Shield for LTSH Tube by Ladhani Metal Corporation – manufacturer, supplier, and exporter – is a dependable solution for protecting tube surfaces in moderately corrosive, abrasive, and thermally active environments. Its martensitic stainless composition and mechanical durability make it ideal for power plants and process boilers requiring extended service life with lower maintenance needs. For customized dimensions, technical support, or quotation, contact Ladhani Metal Corporation.

Half Round Tube Shield Half Round Tube Shields by Ladhani Metal Corporation are designed to protect heat exchange surfaces such as boiler tubes, superheaters, and economizer coils from erosion, scaling, impact from ash particles, and flue gas corrosion. These shields are commonly applied in power plants, waste heat recovery boilers, and industrial heating systems to increase the service life of tubes and improve overall system reliability. Their semi-cylindrical shape ensures a snug fit over tube surfaces, especially in zones exposed to high-velocity gas flow or particulate matter. SS 410 Half Round Tube Shield for LTSH Tube The SS 410 Half Round Tube Shield is manufactured from martensitic stainless steel grade 410. This material offers high mechanical strength, moderate corrosion resistance, and excellent resistance to wear and oxidation in mildly corrosive and thermal environments. Specifically developed for Low Temperature Superheater (LTSH) applications, the SS 410 shield provides effective surface protection against soot, fly ash, and erosive gas streams where thermal and mechanical stresses are present. The Low Temperature Superheater (LTSH) is a section in a boiler where saturated steam from the steam drum is superheated to a moderately higher temperature before entering the high-temperature superheater stages. Positioned in areas with relatively lower flue gas temperatures, the LTSH helps improve thermal efficiency and reduces moisture content in steam. Due to constant exposure to abrasive flue gases and ash, LTSH tubes are prone to wear and require protective shielding, such as half round tube shields, to extend service life. Ladhani Metal Corporation is a trusted manufacturer, supplier, and exporter of SS 410 Half Round Tube Shields for LTSH applications, offering durable, cost-effective protection in thermal and industrial systems. Chemical Composition of SS 410 – Martensitic Stainless Steel • Carbon (C): 0.08 – 0.15% • Manganese (Mn): ≤ 1.00% • Phosphorus (P): ≤ 0.040% • Sulfur (S): ≤ 0.030% • Silicon (Si): ≤ 1.00% • Chromium (Cr): 11.5 – 13.5% • Nickel (Ni): ≤ 0.75% • Iron (Fe): Balance Applications: Suitable for low-temperature superheater zones exposed to fly ash erosion, oxidation, mechanical abrasion, and light corrosion. Uses • Installed on LTSH tube surfaces in power boilers to protect against particulate erosion and flue gas impact • Shields return bends and convection coils in HRSGs and WHRBs exposed to fluctuating gas temperatures • Used in process boilers and steam generators handling slightly corrosive or abrasive flue gases • Effective for dry ash and solid particulate protection in coal and biomass-fired units • Ideal for applications where wear resistance and moderate corrosion protection are critical Features • High mechanical strength – Withstands erosion, abrasion, and mechanical stress in high-flow zones • Moderate corrosion and oxidation resistance – Suitable for dry and mildly corrosive flue gas streams • Custom-fit – Fabricated to match the diameter, curvature, and layout of LTSH tubes • Easy installation – Compatible with weld-on, clamp-on, or banding installation methods • Cost-effective protection – Durable performance at an economical price point • Available in multiple lengths, thicknesses, and tube radii as per application needs Applications • thermal power plants – Protects LTSH tubes from fly ash impact and erosion in dry flue gas paths • waste heat recovery boilers – Applied in low-temperature return sections vulnerable to mechanical wear • steam generation systems – Shields superheater tubes operating in abrasive flue gas conditions • coal-fired boilers – Guards against slag and ash erosion in lower convection zones • process and utility boilers – Extends tube life in units operating with solid fuel combustion Conclusion The SS 410 Half Round Tube Shield for LTSH Tube by Ladhani Metal Corporation – manufacturer, supplier, and exporter – offers reliable, abrasion-resistant protection for superheater and boiler tubes in low-temperature flue gas environments. With its excellent wear resistance and mechanical durability, it is a practical choice for enhancing system performance and reducing downtime in power and industrial boilers. For custom sizing, technical guidance, or quotations, please contact Ladhani Metal Corporation.

Half Round Tube Shield Half Round Tube Shields by Ladhani Metal Corporation are protective components engineered to shield boiler tubes, superheaters, and heat exchangers from erosion, scaling, and ash impact. These shields are widely used in thermal power plants, industrial steam systems, and waste heat recovery units to prolong tube life and enhance operational reliability. Their semi-cylindrical shape allows for easy installation over exposed tube surfaces, especially in zones exposed to abrasive flue gases and thermal stress. SS 310S Half Round Tube Shield for LTSH Tube The SS 310S Half Round Tube Shield is manufactured from low-carbon austenitic stainless steel grade 310S. With high chromium and nickel content, it offers excellent resistance to oxidation and scaling at elevated temperatures, while its reduced carbon level enhances weldability and reduces the risk of sensitization. This makes it ideal for Low Temperature Superheater (LTSH) applications, where tubes are exposed to flue gas streams, ash particles, and moderate thermal cycling. The Low Temperature Superheater (LTSH) is a section in a boiler where saturated steam from the steam drum is superheated to a moderately higher temperature before entering the high-temperature superheater stages. Positioned in areas with relatively lower flue gas temperatures, the LTSH helps improve thermal efficiency and reduces moisture content in steam. Due to constant exposure to abrasive flue gases and ash, LTSH tubes are prone to wear and require protective shielding, such as half round tube shields, to extend service life. Ladhani Metal Corporation is a trusted manufacturer, supplier, and exporter of SS 310S Half Round Tube Shields for LTSH tubes, offering high-performance shielding solutions for long-term service in boiler and heat recovery systems. Chemical Composition of SS 310S – Low Carbon Austenitic Stainless Steel • Carbon (C): ≤ 0.08% • Manganese (Mn): ≤ 2.00% • Phosphorus (P): ≤ 0.045% • Sulfur (S): ≤ 0.030% • Silicon (Si): ≤ 1.50% • Chromium (Cr): 24.0 – 26.0% • Nickel (Ni): 19.0 – 22.0% • Iron (Fe): Balance Applications: Suitable for areas with exposure to moderate temperatures, oxidizing gases, and ash deposition where high-temperature strength and corrosion resistance are critical. Uses • Protects LTSH tubes in power boilers from ash erosion, soot impact, and flue gas corrosion • Used in convection zones of HRSGs, economizers, and waste heat recovery units • Shields tube surfaces in steam generation systems exposed to gas turbulence and thermal cycling • Effective in industrial heating systems and chemical boilers facing scale formation and heat stress • Enhances durability of tubes in coal-fired and biomass-fired boilers with fly ash carryover Features • Excellent oxidation and scaling resistance – Performs in oxidizing environments and thermal zones • Superior weldability – Low carbon content minimizes risk of intergranular corrosion during welding • Tailored protection – Custom-fabricated to match tube diameter, bend radius, and system layout • Simple installation – Compatible with clamping, banding, or welding methods for quick setup • Extended tube life – Minimizes erosion and surface degradation, reducing maintenance downtime • Available in various lengths and thicknesses per system requirements Applications • thermal power plants – Installed on LTSH tube banks for long-term protection against erosion and corrosion • waste heat recovery boilers – Shields curved tubes in return flow zones with ash-laden flue gas • petrochemical units – Applied on steam coils and heat exchanger tubes operating under oxidizing gas exposure • utility boilers – Protects superheater tubes from scaling and particulate impact in low-temperature sections • industrial boiler systems – Enhances performance and service life of steam tubes in energy recovery zones Conclusion The SS 310S Half Round Tube Shield for LTSH Tube by Ladhani Metal Corporation – manufacturer, supplier, and exporter – offers reliable protection for superheater tubes operating in low-temperature, oxidizing, and abrasive flue gas environments. With enhanced weldability, high-temperature resistance, and custom-fit fabrication, this shield ensures dependable performance across a wide range of thermal and industrial applications. For technical assistance, tailored designs, or quotation requests, please contact Ladhani Metal Corporation.

Half Round Tube Shield Half Round Tube Shields by Ladhani Metal Corporation are designed to protect boiler coils, heat exchanger tubes, and superheaters from erosion, scaling, slag deposition, and high-temperature damage. These shields are used extensively in thermal power plants, waste heat recovery systems, and process industries to extend tube life, reduce maintenance costs, and maintain thermal efficiency. Their semi-cylindrical design allows for easy and secure installation over straight or curved tube surfaces. 1Cr13 U Type Inner Half Round Tube Shield The 1Cr13 U Type Inner Half Round Tube Shield is fabricated from martensitic stainless steel 1Cr13, offering good mechanical strength, moderate corrosion resistance, and excellent wear resistance. This grade performs well in thermal systems subject to moderate chemical exposure and mechanical erosion. The inner U-type configuration is engineered to shield the inner arc of U-bend tubes, where turbulent flow, thermal cycling, and slag buildup are most intense and damaging. • Inner U Type Half Round Tube Shield – Covers the internal curvature of U-bend tubes, protecting against erosion, slag impact, and thermal degradation in high-flow areas. Ladhani Metal Corporation is a trusted manufacturer, supplier, and exporter of 1Cr13 U Type Inner Half Round Tube Shields, offering durable and cost-effective solutions for general-purpose heat protection in industrial systems. Chemical Composition of 1Cr13 – Martensitic Stainless Steel • Carbon (C): ≤ 0.15% • Manganese (Mn): ≤ 1.00% • Phosphorus (P): ≤ 0.035% • Sulfur (S): ≤ 0.030% • Silicon (Si): ≤ 1.00% • Chromium (Cr): 12.0 – 14.0% • Iron (Fe): Balance Applications: Suitable for moderately corrosive and abrasive environments with thermal exposure, where strength and erosion resistance are required. Uses • Installed on the inner arc of U-bend tubes in boilers and reheaters to resist erosion from flue gas flow • Shields inner bends in WHRBs and HRSGs subjected to scale buildup and thermal fatigue • Applied in curved tube sections of heat exchangers and evaporators operating under fluctuating temperatures • Used in process industries for protection against moderate corrosion and mechanical wear • Ideal for thermal units in power, petrochemical, and refining applications Features • Good wear and erosion resistance – Suitable for high-velocity gas flow zones • Inner arc protection – Shields critical U-bend areas where slag, turbulence, and thermal load are most severe • Moderate corrosion resistance – Performs well in mildly aggressive gas environments • Tailored fit – Custom-fabricated to match tube size and bend radius for precise protection • Easy installation – Compatible with clamp-on, weld-on, or banding methods • Cost-effective – An economical solution for routine protection of thermal system tube bends Applications • power generation – Inner U-bend protection in superheaters and economizers facing gas flow and scaling • waste heat recovery – Used in WHRBs to protect return bends from erosion and thermal damage • petrochemical processing – Applied in internal bends of steam reformers and exchangers • chemical industry – Suitable for use in reactors and thermal units operating under moderate heat and chemical exposure • industrial furnaces – Protects tube bends from slag deposits and temperature fluctuations Conclusion The 1Cr13 U Type Inner Half Round Tube Shield by Ladhani Metal Corporation – manufacturer, supplier, and exporter – offers reliable protection for U-bend tubes exposed to moderate thermal and erosive conditions. With its martensitic strength, wear resistance, and affordable performance, it is well-suited for a wide range of thermal and industrial process applications. For custom sizes, technical guidance, or quotations, please contact Ladhani Metal Corporation.

Half Round Tube Shield Half Round Tube Shields by Ladhani Metal Corporation are protective components designed to guard heat exchanger coils, boiler tubes, and superheater assemblies from erosion, high-temperature scaling, slag accumulation, and corrosion. These shields are vital in high-performance industrial systems, including power plants, refineries, and chemical process units. Their half-round shape allows easy installation on both straight and curved tubes, improving system longevity while minimizing downtime and maintenance frequency. 1Cr20Ni14Si2 U Type Inner Half Round Tube Shield The 1Cr20Ni14Si2 U Type Inner Half Round Tube Shield is manufactured using a high-temperature austenitic stainless steel alloy with enhanced chromium, nickel, and silicon content. This alloy delivers excellent oxidation resistance, thermal fatigue resistance, and structural stability at elevated temperatures. The inner U-type configuration is tailored to cover the inner arc of U-bend tubes, offering critical protection where high-velocity gas, turbulence, and slag deposits can rapidly wear or degrade tube surfaces. • Inner U Type Half Round Tube Shield – Designed to protect the inner curvature of U-bend tubes from scaling, erosion, and heat-related damage in thermal systems. Ladhani Metal Corporation is a leading manufacturer, supplier, and exporter of 1Cr20Ni14Si2 U Type Inner Half Round Tube Shields, delivering high-performance shielding solutions for demanding high-temperature environments. Chemical Composition of 1Cr20Ni14Si2 – High Chromium-Nickel-Silicon Heat-Resistant Alloy • Carbon (C): ≤ 0.20% • Manganese (Mn): ≤ 1.50% • Phosphorus (P): ≤ 0.035% • Sulfur (S): ≤ 0.030% • Silicon (Si): 1.80 – 2.50% • Chromium (Cr): 19.0 – 21.0% • Nickel (Ni): 13.0 – 15.0% • Iron (Fe): Balance Applications: Ideal for continuous high-temperature operations involving oxidizing or sulfur-containing gases. Well-suited for applications requiring excellent heat resistance and minimal thermal deformation. Uses • Shields inner arcs of U-bend tubes in boilers and superheaters operating at elevated temperatures • Installed in WHRBs and HRSGs to prevent scaling, slag, and erosion in internal tube bends • Used in curved coils in reformers and process heaters exposed to hot gas and thermal cycling • Protects tube bends in chemical reactors, incinerators, and industrial furnaces from oxidation and surface degradation • Effective in systems where stability at high temperatures and resistance to carburizing and sulfidizing environments are essential Features • Excellent high-temperature performance – Withstands long-term exposure to temperatures exceeding 1000°C • Inner arc coverage – Precisely shields erosion-prone internal tube bends in critical heat transfer zones • Superior oxidation and scaling resistance – Resists corrosion in aggressive combustion gas atmospheres • Custom-fit design – Fabricated according to specified tube radii and diameters for optimal coverage and secure fit • Quick and secure installation – Compatible with clamping, banding, or tack welding methods • Long operational life – Reduces the frequency of tube failures, improving reliability and plant efficiency Applications • power plants – Installed on U-bend tubes in superheaters and reheaters facing continuous high-temperature service • petrochemical plants – Protects inner arcs of tubes in reformers and gas processing heat exchangers • waste heat recovery – Shields return bends in WHRBs and HRSGs exposed to hot flue gas and slag • thermal processing – Applied in furnaces and incinerators where hot combustion gases affect internal tube surfaces • chemical industry – Guards against oxidizing and corrosive gas damage in curved tube sections of reactors Conclusion The 1Cr20Ni14Si2 U Type Inner Half Round Tube Shield by Ladhani Metal Corporation – manufacturer, supplier, and exporter – is a robust and heat-resistant solution for protecting U-bend tubes in high-temperature and chemically aggressive conditions. Its high alloy composition, excellent thermal resistance, and customized fitment make it ideal for enhancing tube performance and reliability in critical thermal systems. For technical specifications, customized fabrication, or quotations, please contact Ladhani Metal Corporation.

Half Round Tube Shield Half Round Tube Shields by Ladhani Metal Corporation are engineered to protect the surfaces of boiler tubes, superheaters, and heat exchanger coils from high-temperature corrosion, erosion, slag deposition, and scaling. Widely used in power generation, petrochemical, and industrial processing systems, these shields are fabricated with a half-round profile that allows quick installation over curved or straight tube surfaces, extending service life and minimizing repair and replacement needs. Cr23Ni13 U Type Inner Half Round Tube Shield The Cr23Ni13 U Type Inner Half Round Tube Shield is manufactured from a chromium-nickel austenitic alloy known for its excellent high-temperature resistance, structural stability, and corrosion resistance. It performs reliably under continuous thermal exposure and is well-suited for systems exposed to oxidizing, carburizing, and sulfur-rich gases. The inner U-type configuration is designed specifically to shield the inner arc of U-bend tubes, which are more susceptible to localized turbulence, thermal fatigue, and scale formation. • Inner U Type Half Round Tube Shield – Covers the internal curvature of U-bend tubes, providing targeted protection from flue gas erosion, thermal scaling, and corrosion. Ladhani Metal Corporation is a leading manufacturer, supplier, and exporter of Cr23Ni13 U Type Inner Half Round Tube Shields, offering precision-engineered solutions for high-performance thermal and chemical systems. Chemical Composition of Cr23Ni13 – Austenitic Heat-Resistant Steel • Carbon (C): ≤ 0.12% • Manganese (Mn): ≤ 1.50% • Phosphorus (P): ≤ 0.035% • Sulfur (S): ≤ 0.030% • Silicon (Si): ≤ 1.50% • Chromium (Cr): 22.0 – 24.0% • Nickel (Ni): 12.0 – 14.0% • Iron (Fe): Balance Applications: Suitable for continuous exposure to high temperatures in oxidizing and chemically aggressive environments. Ideal for inner bend protection in return coil systems subjected to high thermal load and corrosive gas flow. Uses • Protects inner arcs of U-bend tubes in thermal power plant superheaters, reheaters, and economizers • Installed in WHRBs and HRSGs to resist scale and slag in return bends exposed to flue gas turbulence • Applied in steam reformers, process furnaces, and heat exchangers where inner tube surfaces face corrosive and hot gas impact • Used in chemical reactors and cracking units operating under cyclic thermal and chemical stress • Suitable for long-term protection of curved tubes in industrial combustion and heating equipment Features • High-temperature oxidation resistance – Performs in continuous service above 1000°C • Inner arc shielding – Targets protection for the most erosion-prone and heat-stressed tube area • Corrosion resistance – Withstands exposure to sulfur-rich gases, acidic vapors, and flue gas byproducts • Fabricated to specification – Available in custom sizes and bend radii for a precise fit and stable coverage • Simple installation – Can be secured using clamping, banding, or welding without disrupting the system • Extended service life – Reduces risk of tube failure, minimizes maintenance downtime, and improves system efficiency Applications • thermal and power generation – Protects inner U-bend surfaces from corrosion and erosion in steam circuits • petrochemical processing – Shields return bends in reformers and exchangers from hot process gases • waste heat recovery – Used in curved tubes of WHRBs and HRSGs for inner arc scale protection • chemical industry – Applied in reactors and thermal systems subjected to chemical vapors and high heat • furnace and incineration systems – Effective in resisting slag and gas-induced wear in industrial burners Conclusion The Cr23Ni13 U Type Inner Half Round Tube Shield by Ladhani Metal Corporation – manufacturer, supplier, and exporter – offers dependable inner arc protection for U-bend tubes operating in aggressive thermal and chemical environments. Its high-temperature and corrosion-resistant properties make it ideal for safeguarding critical process tubes across a range of high-performance industrial systems. For technical consultation, customized fabrication, or quotations, please contact Ladhani Metal Corporation.

Half Round Tube Shield Half Round Tube Shields by Ladhani Metal Corporation are high-performance protective components engineered to safeguard boiler tubes, heat exchanger coils, and superheaters from erosion, thermal fatigue, scaling, and corrosion. Widely used in thermal power plants, petrochemical units, and process heating systems, these shields offer reliable surface protection in extreme environments. Their half-round design allows quick installation over both curved and straight tube sections, extending tube life and minimizing maintenance requirements. Cr25Ni20 U Type Inner Half Round Tube Shield The Cr25Ni20 U Type Inner Half Round Tube Shield is made from a high-alloy chromium-nickel austenitic stainless steel that offers outstanding resistance to oxidation, carburization, and high-temperature corrosion. This alloy is well suited for environments involving thermal cycling and chemically aggressive gases. The inner U-type configuration is specifically designed to protect the inside curvature of U-bend tubes—where gas turbulence, thermal stress, and slag accumulation can lead to premature wear and damage. • Inner U Type Half Round Tube Shield – Designed to guard the inner arc of U-bend tubes against erosion, scaling, and oxidation under high thermal loads and gas flow impact. Ladhani Metal Corporation is a trusted manufacturer, supplier, and exporter of Cr25Ni20 U Type Inner Half Round Tube Shields, delivering precision-engineered solutions for demanding heat and corrosion environments. Chemical Composition of Cr25Ni20 – High Chromium-Nickel Austenitic Alloy • Carbon (C): ≤ 0.20% • Manganese (Mn): ≤ 2.00% • Phosphorus (P): ≤ 0.040% • Sulfur (S): ≤ 0.030% • Silicon (Si): ≤ 1.50% • Chromium (Cr): 24.0 – 26.0% • Nickel (Ni): 19.0 – 22.0% • Iron (Fe): Balance Applications: Ideal for high-temperature applications involving oxidizing, carburizing, or sulfidizing gases, where mechanical and chemical durability is critical. Uses • Shields inner arcs of U-bend tubes in boilers and superheaters exposed to oxidizing combustion gases • Protects return bends in waste heat recovery boilers (WHRBs) and heat recovery steam generators (HRSGs) • Applied in curved tubes in reformers, incinerators, and heat exchangers operating above 900°C • Used in chemical and petrochemical systems with chloride- or sulfur-laden atmospheres • Suitable for tube protection in high-temperature furnaces and metallurgical processes Features • Excellent high-temperature oxidation resistance – Performs reliably at sustained service temperatures up to 1150°C • Inner arc protection – Focused shielding of the bend area most affected by thermal cycling and gas turbulence • Corrosion and scaling resistance – Maintains integrity in aggressive chemical and flue gas environments • Precision engineering – Custom-manufactured to match specific tube diameter and bend geometry • Easy to install – Compatible with clamp-on, tack welding, or stainless steel banding • Durable and long-lasting – Reduces frequency of tube failures and downtime in critical systems Applications • power generation – Used in superheater U-bends where inner arcs are exposed to extreme thermal loads • petrochemical and fertilizer plants – Shields inner return bends in steam reformers and reactors • waste heat recovery – Installed in WHRBs and HRSGs to prevent scaling and oxidation on inner bend surfaces • chemical process industry – Protects U-bend tubes from acid vapors, hot gases, and corrosion • metallurgical industry – Ideal for inner arc protection in high-temperature treatment furnaces Conclusion The Cr25Ni20 U Type Inner Half Round Tube Shield by Ladhani Metal Corporation – manufacturer, supplier, and exporter – offers robust protection for U-bend tubes operating in high-temperature and corrosive environments. Its exceptional resistance to oxidation and thermal damage makes it ideal for critical industrial systems requiring long-lasting performance and reliability. For detailed specifications, custom fabrication, or quotations, please contact Ladhani Metal Corporation.

Half Round Tube Shield Half Round Tube Shields by Ladhani Metal Corporation are precisely engineered components used to safeguard boiler tubes, superheaters, and heat exchanger coils from erosion, scaling, thermal stress, and high-temperature corrosion. Their half-round construction enables quick and secure installation over straight or curved tube surfaces, offering long-term protection and minimizing maintenance in industrial heating systems, power plants, and petrochemical facilities. 1Cr18Ni9Ti U Type Inner Half Round Tube Shield The 1Cr18Ni9Ti U Type Inner Half Round Tube Shield is manufactured from a titanium-stabilized austenitic stainless steel grade, offering superior resistance to intergranular corrosion and oxidation at elevated temperatures. This grade is particularly effective in welded applications and thermal systems subjected to cycling and corrosive media. The inner U-type configuration is designed to shield the inside curvature of U-bend tubes, where turbulent gas flow, slag, and thermal concentration often cause accelerated wear and scaling. • Inner U Type Half Round Tube Shield – Designed to protect the internal arc of U-bend tubes from high-temperature scaling, slag impact, and turbulent gas erosion. Ladhani Metal Corporation is a trusted manufacturer, supplier, and exporter of 1Cr18Ni9Ti U Type Inner Half Round Tube Shields, offering durable, high-performance shielding solutions for critical thermal systems. Chemical Composition of 1Cr18Ni9Ti – Titanium-Stabilized Austenitic Stainless Steel • Carbon (C): ≤ 0.12% • Manganese (Mn): ≤ 2.00% • Phosphorus (P): ≤ 0.035% • Sulfur (S): ≤ 0.030% • Silicon (Si): ≤ 1.00% • Chromium (Cr): 17.0 – 19.0% • Nickel (Ni): 8.0 – 11.0% • Titanium (Ti): Stabilized as required • Iron (Fe): Balance Applications: Ideal for welded and high-temperature systems exposed to oxidation, intergranular corrosion, and chloride-bearing flue gases. Uses • Protects inner arcs of U-bend tubes in superheaters and reheaters of thermal power plants • Installed in return bends of waste heat recovery boilers (WHRBs) and HRSGs facing slag and scale accumulation • Applied in curved tube sections in chemical reactors and heat exchangers exposed to acidic or oxidizing gases • Suitable for marine and coastal heating systems where chlorides and moisture are present • Used in food processing, metallurgical furnaces, and process plants requiring stable, high-temperature performance Features • Excellent intergranular corrosion resistance – Stabilized with titanium to prevent carbide precipitation • Inner arc protection – Shields high-stress areas from gas turbulence and heat-induced damage • High-temperature performance – Reliable up to 870°C in oxidizing environments • Custom fit – Fabricated to match specific tube diameters and bend radii for precise installation • Easy to install – Suitable for clamp-on, weld-on, or banding methods • Long service life – Reduces frequency of tube replacement and supports consistent thermal performance Applications • thermal power generation – Inner arc protection in U-bend tubes exposed to combustion gases and temperature fluctuations • petrochemical and fertilizer plants – Shields tube bends in reactors and reformers exposed to acidic gases • waste heat recovery – Guards inner surfaces of tube coils in WHRBs and HRSGs from scaling and corrosion • marine heat exchangers – Suitable for use in systems exposed to saltwater vapors and high humidity • industrial furnaces and incinerators – Provides internal bend protection under severe thermal cycling Conclusion The 1Cr18Ni9Ti U Type Inner Half Round Tube Shield by Ladhani Metal Corporation – manufacturer, supplier, and exporter – delivers robust and reliable protection for U-bend tubes operating in corrosive and high-temperature environments. With titanium stabilization and a custom-engineered fit, this shield ensures extended tube life, reduced wear, and optimized performance in industrial heating systems. For technical assistance, custom specifications, or quotations, please contact Ladhani Metal Corporation.

Half Round Tube Shield Half Round Tube Shields by Ladhani Metal Corporation are designed to protect heat exchanger tubes, boiler coils, and superheater assemblies from erosion, scaling, and surface degradation in high-temperature and corrosive environments. These shields are used extensively in power plants, chemical processing units, and industrial heating systems. Their half-round construction enables fast and secure installation over both straight and curved tube surfaces, providing an effective barrier against damage from flue gas, slag, and particulate impact. SS 430 U Type Inner Half Round Tube Shield The SS 430 U Type Inner Half Round Tube Shield is manufactured from ferritic stainless steel grade 430, known for its good corrosion resistance, excellent thermal conductivity, and oxidation resistance. It performs reliably in moderate-temperature applications and provides dependable protection against scaling and surface deterioration. The inner U-type configuration is specifically engineered to cover the inside arc of U-bend tubes, which are particularly vulnerable to high-velocity gas flow and localized heat concentration. • Inner U Type Half Round Tube Shield – Covers the internal curvature of U-bend tubes to guard against turbulence-driven erosion, slag buildup, and scaling in thermal systems. Ladhani Metal Corporation is a leading manufacturer, supplier, and exporter of SS 430 U Type Inner Half Round Tube Shields, offering reliable protection components for heat-exposed industrial systems. Chemical Composition of SS 430 – Ferritic Stainless Steel • Carbon (C): ≤ 0.12% • Manganese (Mn): ≤ 1.00% • Phosphorus (P): ≤ 0.040% • Sulfur (S): ≤ 0.030% • Silicon (Si): ≤ 1.00% • Chromium (Cr): 16.0 – 18.0% • Nickel (Ni): ≤ 0.75% • Iron (Fe): Balance Applications: Suitable for moderately corrosive and oxidizing environments where high thermal conductivity and scaling resistance are required, especially in non-welded systems. Uses • Installed on inner arc of U-bend tubes in boiler and superheater coils subject to flue gas turbulence • Protects return bends in WHRBs and HRSGs from surface degradation and slag impact • Used in heat exchangers and process heaters with moderate corrosion and temperature exposure • Applied in thermal processing plants, food-grade heating systems, and chemical units • Effective for curved coil protection in dryers, economizers, and incinerator heat recovery sections Features • Good corrosion and oxidation resistance – Performs well in moderately aggressive environments • Inner arc coverage – Specifically shields areas affected by heat, scale, and turbulent flow • Cost-effective – Offers a balance between performance and affordability for general-purpose applications • Thermal stability – Maintains structural integrity at service temperatures up to 815°C • Custom-fabricated – Tailored to match specific tube bend radius and outer diameter for secure fit • Easy installation – Compatible with clamp-on, banding, or weld-on mounting for fast and efficient assembly Applications • power generation – Used in superheater and economizer return bends to prevent scale and erosion • chemical and food industry – Applied in heat recovery systems requiring corrosion-resistant inner arc protection • waste heat recovery – Installed in WHRB and HRSG curved tubes to reduce slag and flue gas impact • dryers and kilns – Shields inner U-bend tubes in rotating or stationary heating equipment • process heating units – Provides mechanical and thermal protection for tubes exposed to oxidizing gas streams Conclusion The SS 430 U Type Inner Half Round Tube Shield by Ladhani Metal Corporation – manufacturer, supplier, and exporter – is a reliable and economical solution for protecting the inner arcs of U-bend tubes in moderately corrosive and thermal environments. With its ferritic composition, good thermal performance, and ease of installation, it is ideal for general-purpose heat system applications. For technical assistance, customized dimensions, or quotations, please contact Ladhani Metal Corporation