Product name:Titanium Dished Head
Standard: ASME VIII-I, DIN28013
Material: Titanium GR1, GR2
Size: Customized
Titanium Dished Head
The most common dish heads are the Ellipsoidal head the Hemispherical head. Heads are widely used in heat exchanger/pressure vessel equipment such as power generation, seawater desalination, water treatment, chemical processing and oil and gas exploration industries.
Product name:
Titanium dished head
Standard: According to DIN28013
Grade: GR1, GR2
Quality Inspection: 100% Ultrasonic Test and PT test after forming.
Process: Cold forming and Hot forming
Fabrication: According to ASME VIII-I standard.
Application:Used for Pressure Vessel Equipment
Classification of the head
Ellipsoid head, hemispherical head and hyperboloid head are three types of ASME pressure vessel disc head.
Ellipsoidal head
This is also known as a 2:1 oval head. This head shape is more economical because the height of the head is only a quarter of its diameter. Its radius varies between the major axis and the minor axis.
Hemispherical head
A sphere is the ideal shape for the head because the pressure in the container is evenly distributed over the surface of the head. The head radius (R) is equal to the radius of the cylindrical part of the container.
Spherical head of complex surface
These have a disc head with a fixed radius (CR), the size of which depends on the type of spherical head. The transition between the cylinder and the plate is called the knuckle. The steering knuckle is circular.
Chemical composition (Wt%)
ASTM No.
Fe max
O max
N max
C max
H max
Pd
Al
Bal
Grade 1
0.2
0.18
0.03
0.1
0.015
-
-
Ti
Grade 2
0.3
0.25
0.03
0.1
0.015
-
-
Ti
Physical Properties (Min)
ASTM Grade
Alloy Composition
Tensile Strength
Yield Strength
Elongation min %
ksi
Mpa
ksi
Mpa
Grade 1
Unalloyed Ti ("Pure") 35A -CP1
35
240
25
170
30
Grade 2
Unalloyed Ti ("Pure") 50A -CP2
58
400
40
275
25
Product Name: Titanium Anode Basket
Material: Gr1, Gr2
Size: Customized
Application: Anodizing Electroplating Plating
Shape: Rectangular, round and spiral etc
Characteristics
1. Used in the electroplating industry, it can effectively control the ratio of anode to cathode;
2. The anode has good solubility and produces less anode mud;
3. It is convenient to load or supplement anode materials;
4. The anode material is fully used, saving energy consumption;
5. Titanium basket has the characteristics of acid resistance, alkali resistance, corrosion resistance, high temperature resistance and high strength;
6. Titanium basket uses a mesh drawn from industrial pure titanium plates, which has high tensile strength and durability.
Chemical composition (Wt%)
ASTM No.
Fe max
O max
N max
C max
H max
Pd
Al
Bal
Grade 1
0.2
0.18
0.03
0.1
0.015
-
-
Ti
Grade 2
0.3
0.25
0.03
0.1
0.015
-
-
Ti
Physical Properties (Min)
ASTM Grade
Alloy Composition
Tensile Strength
Yield Strength
Elongation min %
ksi
Mpa
ksi
Mpa
Grade 1
Unalloyed Ti ("Pure") 35A -CP1
35
240
25
170
30
Grade 2
Unalloyed Ti ("Pure") 50A -CP2
58
400
40
275
25
Titanium jigs for plating
Any project to anodize requires a reliable hanger/jig/rack, first to prevent it from falling to the bottom of the anodizing tank, and second to allow the current to be safely transferred from the jig to the workpiece. Anodic oxidation clamps are usually made of aluminum or titanium. Aluminum fixtures must of course be anodized and must be chemically stripped. Continuous anodizing and stripping can result in short service life, so there is no need to strip titanium after the anodizing process.
Item Name: titanium jig for coating
Size:Customized size is welcomed
Material: Titanium Gr1, Gr2
Application,Electroplating industry
Surface:Sand Blasting, Acid Washing
Parameter:Current density≤2000A/M2
Temperature:<65°C
PH: 0.1~14
Max content of Fluoride ion is 200PPM
Chemical composition (Wt%)
ASTM No.
Fe max
O max
N max
C max
H max
Pd
Al
Bal
Grade 1
0.2
0.18
0.03
0.1
0.015
-
-
Ti
Grade 2
0.3
0.25
0.03
0.1
0.015
-
-
Ti
Physical Properties (Min)
ASTM Grade
Alloy Composition
Tensile Strength
Yield Strength
Elongation min %
ksi
Mpa
ksi
Mpa
Grade 1
Unalloyed Ti ("Pure") 35A -CP1
35
240
25
170
30
Grade 2
Unalloyed Ti ("Pure") 50A -CP2
58
400
40
275
25
Product Name: Titanium jigs and racks
Material: Gr1, Gr2
Application: Electroplating, anodizing etc.
Size: Customized
Surface: Polished
Titanium jigs and racks
Universal jig and racks are suitable for a variety of parts and processes. The form and structure of general electroplating jigs shall be determined according to the geometry of plated parts, technical requirements of plating, process and size of equipment.
Product Name:Titanium jigs and racks
Material: Gr1, Gr2
Application: Electroplating, anodizing etc.
Size: Customized
Surface: Polished
Precautions for use of titanium jigs and racks:
1. The distance from the bottom of titanium hanger to the groove bottom is 150-200mm; The concentration of working immersed electric part liquid is about 40-60mm away from the liquid level of the part.
2. The distance between titanium hanger and hanger surface is 20-40mm; And groove wall shall be greater than 50mm
3. When the titanium tools that can be used are operated manually, the loading weight is generally about 1-3kg; The position of titanium hanging rod shall be more than 80mm away from the liquid level and shall bear the whole load
The features of our titanium jigs and racks:
▲ Accurate size
▲ High corrosion resistance
▲ Cost-effective
▲ Easy to load and unload
▲ Improve electrical conductivity